Multi-arcionplatingceramic/metalmultilayers宝特17-4ph材料 ,lasersurfacealloyingcoatingandhighvelocityoxy-fuel(HVOF)sprayinghardceramicscoatingwerepreparedon17-4PHstainlesssteeltostudytheinfluenceofsurfacetreatmentonsolidparticleerosionresistance17-4PHstainlesssteel.Then,thefailuremechanismofSPEatbothlowandhighimpingementanglesof17-4PHstainlesssteelandthreekindsofcoatingswasstudiedbysurfacescratchestesterandsmallenergymulti-impacttestmachine.TheresultsindicatethatthemainfailuremechanismoftheSPEatlowimpingementangleon17-4PHstainlesssteelandcoatingsisthemicro-cuttingmode;butatahighangle宝特17-4ph材料 ,themainmechanismisthemulti-impactfatiguefailuremode.TheSPEresistanceof17-4PHstainlesssteelat30°and90°impingementanglesisremarkablyimprovedbytheHVOFWC-17Cocoating.ThelaseralloyingcoatingalsoenhancestheSPEresistanceof17-4PHstainlesssteelatboth30°and90°impingementanglesrespectively,butthecomprehensiveperformanceofthelaseralloyingcoatingisinferiorthanthatofHVOFWC-17Cocoating.However,theTiAlN/TimultilayerdoesnotimprovetheSPEresistanceof17-4PHstainlesssteelat30°and90°impingementangles.。

17-4PH不锈钢常规热处理工艺为固溶处理十时效处理，该钢合金含量高、淬透性***好，空冷即可获得马氏体组织，但组织中还存在一定量残余奥氏体。

因此不锈钢630是不是17-4ph，必须通过提高钢的强度，在时效过程中，残余奥氏体分解，部分碳化物析出，17-4不锈钢***佳的固溶温度为1040度，其硬度随时效温度的上升先升后降，***佳热处理工艺为1040度固溶+460度时效保温2h。

温度过低时，奥氏体转化不完全，会使组织中含有较多的铁素体，且难以均匀化；过高的温度则会增加高温铁素体的含量，降低Ms低，增加冷却至室温后残余奥氏体的含量，从而降低硬度值，保温时间根据式样大小和尺寸为0。

0h不等，***后的冷却方式根据不同的性能要求可选用水淬、油淬或空冷；***佳时效温度为度，保温时间控制在24h，温度越高，硬度达到峰值的时间越短。

17-4PH不锈钢具有高的耐蚀性、硬度和耐磨性等优点，但在酸、碱、高温等耐磨性和耐蚀性要求高的工作环境下，其综合性能仍不能满足使用要求，需要强化其表面性能，如表面硬度、耐磨性和疲劳强度。

目前使用较为广泛的表面强化工艺为氮化处理，包括离子渗氮和盐浴符合氮化处理等。

采用离子渗氮时，渗氮温度，时间和氮势会影响材料的基体硬度，氮势和渗氮时间对渗层渗氮有影响，而离子渗氮工艺参数对渗层的表面硬度则无明显的影响。

供货状态有两种：17-4PH不锈钢板厚度0.8–260mm；。

热加工温度1180℃，开始温度1150，终止温度1040℃，空冷或中砂冷。

固溶温度以1040℃恒温2小时，油冷，硬度28-30HRC，水冷，硬度32-35HRC。

此时17-4PH金相组织为低碳马氏体，在此硬度下可进行切削加工。

高温回火温度750℃，炉冷或空冷，硬度28-32HRC。